Seamless thick-walled tubes
Seamless tubes from high-strength alloys
Outer Diameter, mm |
maximum length
(m) Wall thickness, mm |
3.5 |
4.0 |
4.5 |
5.0 |
5.5 |
6.0 |
6.5 |
7.0 |
7.5 |
8.0 |
8.5 |
9.0 |
75 |
2.5 |
2.5 |
2.0 |
2.0 |
2.0 |
2.0 |
2.0 |
1.5 |
- |
- |
- |
- |
76 |
2.5 |
2.5 |
2.0 |
2.0 |
2.0 |
2.0 |
2.0 |
1.5 |
- |
- |
- |
- |
80 |
2.5 |
2.5 |
2.0 |
2.0 |
2.0 |
2.0 |
1.5 |
1.5 |
- |
- |
- |
- |
83 |
2.5 |
2.5 |
2.0 |
2.0 |
2.0 |
2.0 |
1.5 |
1.5 |
1.5 |
1.5 |
1.5 |
1.5 |
85 |
2.5 |
2.5 |
2.0 |
2.0 |
2.0 |
2.0 |
1.5 |
1.5 |
1.5 |
1.5 |
1.5 |
1.5 |
89 |
4.0 |
4.0 |
3.5 |
3.5 |
3.5 |
3.5 |
- |
- |
- |
- |
- |
- |
90 |
4.0 |
4.0 |
3.5 |
3.5 |
3.5 |
3.5 |
- |
- |
- |
- |
- |
- | Seamless tubes from middle-strength alloys
Outer Diameter, mm |
maximum length
(m) Wall thickness, mm |
3.5 |
4.0 |
4.5 |
5.0 |
5.5 |
6.0 |
6.5 |
7.0 |
7.5 |
8.0 |
8.5 |
9.0 |
35 |
5.0 |
4.0 |
3.0 |
3.0 |
- |
- |
- |
- |
- |
- |
- |
- |
36 |
5.0 |
4.0 |
3.0 |
3.0 |
- |
- |
- |
- |
- |
- |
- |
- |
38 |
5.0 |
4.0 |
3.0 |
3.0 |
- |
- |
- |
- |
- |
- |
- |
- |
40 |
4.0 |
4.0 |
3.0 |
3.0 |
- |
- |
- |
- |
- |
- |
- |
- |
42 |
4.0 |
4.0 |
3.0 |
2.5 |
2.5 |
2.5 |
- |
- |
- |
- |
- |
- |
45 |
4.0 |
4.0 |
3.0 |
2.5 |
2.5 |
2.5 |
2.5 |
2.5 |
- |
- |
- |
- |
48 |
4.0 |
4.0 |
3.0 |
2.5 |
2.5 |
2.5 |
2.5 |
2.5 |
- |
- |
- |
- |
51 |
4.5 |
4.5 |
4.5 |
4.5 |
4.5 |
4.5 |
4.0 |
4.0 |
4.0 |
3.0 |
2.5 |
2.5 |
53 |
3.0 |
3.0 |
3.0 |
2.5 |
2.5 |
2.5 |
2.5 |
2.5 |
- |
- |
- |
- |
54 |
3.0 |
3.0 |
2.5 |
2.5 |
2.0 |
2.0 |
2.0 |
2.0 |
- |
- |
- |
- |
56 |
3.0 |
3.0 |
2.5 |
2.5 |
2.0 |
2.0 |
2.0 |
2.0 |
- |
- |
- |
- |
57 |
3.0 |
3.0 |
2.5 |
2.0 |
2.0 |
2.0 |
2.0 |
2.0 |
- |
- |
- |
- |
60 |
2.5 |
2.5 |
2.0 |
2.0 |
2.5 |
2.0 |
2.0 |
2.0 |
- |
- |
- |
- |
63 |
2.5 |
2.5 |
2.0 |
2.0 |
2.5 |
2.0 |
2.0 |
2.0 |
- |
- |
- |
- |
65 |
2.5 |
2.5 |
2.0 |
2.0 |
2.5 |
2.0 |
2.0 |
2.0 |
- |
- |
- |
- |
68 |
2.5 |
2.5 |
2.0 |
2.0 |
2.0 |
|
2.0 |
2.0 |
- |
- |
- |
- |
70 |
2.5 |
2.5 |
2.0 |
2.0 |
2.0 |
|
2.0 |
2.0 |
- |
- |
- |
- | 
Machined tubes from Transverse-screw mill 40-80
|